Florentine Paring

The Florentine Paring / Office knife is your go to knife for everything you would do in your hands and not on the cutting board. This means it’s most suitable for precise actions like peeling and garnishing. Our original design, an oval curved handle with stacked discs assembled around the tang of the blade. Delivery time 3-5 weeks.

BLADE LENGTH. 100mm
BLADE WIDTH. 25mm
OVERALL LENGTH. 205mm
APPROX WEIGHT. 65-70gr
STEEL: 14C28N Stainless Steel / XC75 Carbon Steel
HARDNESS: 60 HRC
EDGE: 50/50

 

A1.HANDLE DESIGN
A2.HANDLE MATERIALS AND COLOURS

Choose as many colours and materials as you like and we will design the handle based on your colour and logic preferences. Feel free to leave specific notes at the bottom.

LOGIC
LEATHER SPACERS
MICARTA AND WOOD DISCS
B.BLADE STEEL AND FINISH Compare

Please note carbon blades will rust if not well taken care of

OK
C1.LASER ETCHING
  • + €10
C2.ADD ACCESSORIES
  • -1+

    A handcrafted, tanned or Black natural leather blade guard with an integral, easy lock and release system to keep your knives protected from scratches, humidity and keep your edges sharp. Compatible with Florentine Paring knives and F2 Steak knives.

  • -1+

    A handcrafted, tanned or Black natural leather blade guard with an integral, easy lock and release system to keep your knives protected from scratches, humidity and keep your edges sharp. Compatible with Florentine Paring knives and F2 Steak knives.

C3.NOTES
Images are for illustration purposes only, colours may vary Delivery time 4 - 6 weeks Please note carbon blades will rust if not well taken care of
TOTAL €

STAINLESS STEEL

Satin

A brushed semi-matt finish with vertical lines.

STEEL: 14C28N
HARDNESS: 59-60hrc

Hand Sanded

A semi-matt hand rubbed finish with horizontal lines.

STEEL: 14C28N
HARDNESS: 59-60hrc
COUNTRY OF ORIGIN: Sweden
MILL: sandvik
SHARPENING:

Intermediate, Whetstones or quality sharpening systems recommended.

GENERAL INFORMATION:

Sharpens quite easily and takes a very sharp edge. The alloy offers a good balanced combination of corrosion resistance, edge stability, wear resistance and strength.

EASE OF CARE:

Stainless Steels are forgiving and require relatively little care.

CARBON STEEL

Hand sanded

A semi-matt hand rubbed finish with horizontal lines.

STEEL: XC90
HARDNESS: 59-60hrc

Forced patina

An acid induced protective layer applied on a hand sanded finish.

STEEL: XC90
HARDNESS: 59-60hrc

leopard patina

A patterned protective layer induced by mustard and acid on a hand sanded finish.

STEEL: XC90
HARDNESS: 59-60hrc
COUNTRY OF ORIGIN: France
MILL: Anfor
SHARPENING:

Easy, Whetstones or quality sharpening systems recommended.

GENERAL INFORMATION:

Sharpens very easily and takes a very sharp edge. The alloy offers almost no corrosion resistance and needs to be kept well. However, edge stability, wear resistance and strength are good and will age beautifully with good care.

EASE OF CARE:

Not a very forgiving steel, will rust if not well taken care of.

HIGH CARBON STEEL

Hand Sanded Forced Patina

An acid induced protective layer applied on a hand sanded finish.

STEEL: C130
HARDNESS: 61+62HRC
COUNTRY OF ORIGIN: France
MILL: Anfor
SHARPENING:

Intermediate (recommended whetstones or quality sharpening systems)

GENERAL INFORMATION:

This steel sharpens quite easily and takes an extremely sharp edge. This alloy offers no corrosion resistance. Because of it's hardness it offers less resistance to chipping or breaks, but has a very high edge holding and strength.

EASE OF CARE:

A very unforgiving steel. Must be well cared for.

STAINLESS STEEL

Satin

A brushed semi-matt finish with vertical lines.

STEEL: 14C28N
HARDNESS: 59-60hrc

Hand sanded

A semi-matt hand rubbed finish with horizontal lines.

STEEL: 14C28N
HARDNESS: 59-60hrc
COUNTRY OF ORIGIN: Sweden
MILL: Sandvik
SHARPENING:

Intermediate, Whetstones or quality sharpening systems recommended.

GENERAL INFORMATION:

Sharpens quite easily and takes a very sharp edge. The alloy offers a good balanced combination of corrosion resistance, edge stability, wear resistance and strength.

EASE OF CARE:

Stainless Steels are forgiving and require relatively little care.

CARBON STEEL

Hand sanded

A semi-matt hand rubbed finish with horizontal lines.

STEEL: XC90
HARDNESS: 59-60hrc

Forced patina

An acid induced protective layer applied on a hand sanded finish.

STEEL: XC90
HARDNESS: 59-60hrc

Leopard patina

A patterned protective layer induced by mustard and acid on a hand sanded finish.

STEEL: XC90
HARDNESS: 59-60hrc
COUNTRY OF ORIGIN: France
MILL: Anfor
SHARPENING:

Easy, Whetstones or quality sharpening systems recommended.

GENERAL INFORMATION:

Sharpens very easily and takes a very sharp edge. The alloy offers almost no corrosion resistance and needs to be kept well. However, edge stability, wear resistance and strength are good and will age beautifully with good care.

EASE OF CARE:

Not a very forgiving steel, will rust if not well taken care of.

STAINLESS STEEL

Satin

A brushed semi-matt finish with vertical lines.

STEEL: 14C28N
HARDNESS: 59-60hrc
COUNTRY OF ORIGIN: Sweden
MILL: Sandvik
SHARPENING:

Intermediate, Whetstones or quality sharpening systems recommended.

GENERAL INFORMATION:

Sharpens quite easily and takes a very sharp edge. The alloy offers a good balanced combination of corrosion resistance, edge stability, wear resistance and strength.

EASE OF CARE:

Stainless Steels are forgiving and require relatively little care.